Is 250 deg for 25 mins the lowest you can/should go? I wonder if doing a longer, lower temp, cure would help with the original hardness of the bullet to stay that way. As it stands now, my bullets loose their hardness after I cure them. I don’t have a hardness tester so I do not know how much, but its enough to tell from scratching it.