It’s possible that could be oxide dross that formed on your melt if it were overheated during the ingot making process, as long as your melt is overheating it will keep forming no matter how many time you flux an try to skim it off.  When remelting the ingots keep the temperature lower and you should be able to flux it back into your melt.